alexa Electrochemical Performance of Mn Doped Co3O4 Supercapacitor: Effect of Aqueous Electrolytes | Open Access Journals
ISSN: 2169-0022
Journal of Material Sciences & Engineering
Make the best use of Scientific Research and information from our 700+ peer reviewed, Open Access Journals that operates with the help of 50,000+ Editorial Board Members and esteemed reviewers and 1000+ Scientific associations in Medical, Clinical, Pharmaceutical, Engineering, Technology and Management Fields.
Meet Inspiring Speakers and Experts at our 3000+ Global Conferenceseries Events with over 600+ Conferences, 1200+ Symposiums and 1200+ Workshops on
Medical, Pharma, Engineering, Science, Technology and Business

Electrochemical Performance of Mn Doped Co3O4 Supercapacitor: Effect of Aqueous Electrolytes

Jogade SM* and Sutrave DS

Department of Electronics, D.B.F Dayanand College of Arts and Science, Solapur, MS, India

*Corresponding Author:
Jogade SM
Department of Electronics
D.B.F Dayanand College of Arts and Science
Solapur, MS, India
Tel: 0217 232 3193
E-mail: m5jogade@gmail.com

Received date: June 16, 2017; Accepted date: June 28, 2017; Published date: June 31, 2017

Citation: Jogade SM, Sutrave DS (2017) Electrochemical Performance of Mn Doped Co3O4 Supercapacitor: Effect of Aqueous Electrolytes. J Material Sci Eng 6: 351. doi: 10.4172/2169-0022.1000351

Copyright: © 2017 Jogade SM, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.

Visit for more related articles at Journal of Material Sciences & Engineering

Abstract

Effect of aqueous electrolytes (KOH, KCl, CH3 COONa and NH4 Cl) on electrochemical behaviour of Supercapacitor was studied by cyclic voltammetry, cyclic stability, and electrochemical impedance analysis. The results show that among all aqueous electrolytes investigated, KOH revealed good supercapacitive behaviour and exhibited 675Fgm-1 specific capacitance, 86% of cyclic stability, 100% columbic efficiency and 8Ω equivalent series resistance ESR.

Keywords

Aqueous electrolytes; KOH; CV; EIS; Specific capacitance; Stability; ESR

Introduction

Supercapacitors, also known as ultracapacitors, electric double layer capacitors (EDLCs) or electrochemical supercapacitors are the electrochemical energy storage devices in which the electric charge is stored in the electrical double layer formed at the interface between electrode and an electrolyte solution. These devices can provide high power capability, excellent reversibility and long cycle life [1-3]. Even though super capacitors are now commercially available, they still require improvements, especially for enhancing their power density and cut the cost at the same time. To reach these objectives, various strategies have been proposed in the literature, involving the development of new materials, new geometries and electrolytes [4].

The electrolyte is the key part of the electrochemical capacitors as the operating voltage, specific capacitance, power density are greatly influenced by the choice of electrolyte. Literature study also indicate that the factors affecting the energy storage capacity of super capacitor are particle size and electrochemical conditions, namely type of electrolyte, concentration of electrolyte, conductivity of the electrolyte, scan rate, etc. [5-9]. Therefore, the electrolytic system must exhibit, a good conductance which determines the power output capability and a good ionic adsorption which determines the specific double-layer capacitance. Overall, the desirable properties of an electrolytic system for super capacitors are high ionic conductivity, wide voltage window, and high electrochemical and thermal stability, low viscosity, low toxicity, low cost, etc. [10]. Compared with non-aqueous electrolytes, the aqueous medium provides a much higher conductivity leading to higher power density. On the other hand, low cost and easy manipulation could be further advantages for aqueous electrolytes.

Until recently, the most commonly used aqueous electrolytes were H2SO4 and KOH [11]. Hence in the present work attempts are made to study various electrochemical properties of supercapacitor with different aqueous electrolytes such as KOH, KCl, CH3COONa and NH4Cl by implementing cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS).

Experimental Section

The supercapacitor cell under test is made up of 1% Manganese doped Cobalt oxide thin film as its working electrode, platinum wire as counter electrode and saturated calomel (SCE) as reference electrode and aqueous electrolyte. The various electrochemical properties of supercapacitor were tested with different aqueous electrolytes such as KOH, KCl, CH3COONa and NH4Cl each of 0.1 M concentration. Thin film electrodes were fabricated by using Sol-gel spin coat deposition technique using stainless steel as substrate. The detailed synthesis and deposition process is discussed in the earlier paper [12].

All characterizations done with the help of CHI608E Electrochemical Workstation. Electrochemical impedance analysis was done by using ZSimpWin Simulation software.

Result and Discussion

Structural properties

The structural analysis of the deposited thin film was done by using X-ray diffractometer varying diffraction angle 2θ from 10° to 90°. Figure 1 shows the X-ray diffraction pattern (XRD) of 1% Mn doped Cobalt oxide thin film. XRD pattern exhibited high intensity diffraction peaks cubic Co3O4 and orthorhombic MnO2 phase. Which indicates film is crystalline in nature. The XRD data were matched with JCPDS card 78-1969 and 82-2169 for cobalt and manganese peaks respectively.

material-sciences-engineering-cobalt-oxide-film

Figure 1: XRD pattern of spin coat deposited 1% Mn doped Cobalt oxide thin film.

Morphological properties

Figure 2 shows the SEM micrographs of Mn-doped Co3O4 films on the stainless steel substrate at two different magnifications ×10,000 and ×40,000. SEM images showed the formation of many tetragonal particles spread smoothly all over the substrate surface. At higher magnification (×40,000), it can be clearly observed that the grains are internally connected with each other and provide porous surface morphology. Average grain size was calculated from the SEM micrographs and it was approximately 0.22 μm.

material-sciences-engineering-micrographs-spin-coat

Figure 2: SEM micrographs of spin coat deposited 1% Mn doped Cobalt oxide thin film.

Electrochemical analysis

Cyclic voltammetry: Figure 3 shows the cyclic voltammetry curves for different aqueous electrolytes KOH, KCl, NH4Cl and CH3COONa. Scan rate is varied from 10 to 100 mV/s. It has been observed from the figures that the optimized potential window and the current density are different for all electrolytes.

material-sciences-engineering-voltammogram-supercapacitor-electrolytes

Figure 3: Cyclic voltammogram curves of supercapacitor for different aqueous electrolytes.

CV Curves for all the electrolytes exhibited a common trend of decreasing specific capacitance values against an increasing scan rate. It is because for very low scan rates the ions have a much longer time to penetrate and reside in the electrode pores and form electric double layers, leading to increase in specific capacitance.

A rectangular type of voltammogram is the indication of ideal capacitive behaviour of any material [13]. But CV curves of KOH and KCl electrolyte showed redox transition peaks at prescribed potentials. This indicates that, the supercapacitive characteristics are mainly governed by Faradaic reactions for these two electrolytes. Whereas no redox peaks were observed on cyclic voltammetry curves of CH3COONa and NH4Cl electrolytes for all scan rates which indicates that the supercapacitive behaviour for these electrolytes is purely based on the electrostatic mechanism and charge-discharge process of active materials occurs at a pseudo-constant rate over a whole potential window [9].

From all the figures, it is also proved that for higher scan rate potential window as well as current associated with the CV curve increases with increase in scan rate. Which indicates that voltammetric current is directly proportional to the scan rates of CV and this is an indication of good supercapacitive behaviour.

Table 1 shows the specific capacitance values with various electrolytes for different scan rates. For KOH electrolyte, which is having high molar conductivity as compared to other eletrolytes [9] highest specific capacitance 675 F/g is observed for that. Whereas KCl exhibited pseudocapacitance nature according to cyclic voltammogram, specific capacitance obtained is 172 F/g at 10 mV/s scan rate. Whereas low specific capacitance of 80 F/g and 56 F/g were obtained for CH3COONa and NH4Cl electrolytes respectively as they have low molar conductivity.

Scan Rate (mV/s) Specific Capacitance (F/g)
KOH KCl CH3COONa NH4Cl
10 675 172 80 56
20 620 163 76 42
40 524 144 65 35
60 465 130 54 30
80 424 124 50 28
100 393 108 43 26

Table 1: Specific Capacitance values for various electrolytes.

Cyclic stability: Retaining of specific capacitance for long redox cycles at higher scan rate operation condition is essential for practical applicability of a supercapacitor. Figure 4 shows the CV curves with KHO, KCl, NH4Cl and CH3COONa electrolytes for 1st and 1000th cycles at the scan rate of 500 mV/s. All Cyclic voltammograms for 1st and 1000th potential cycles showed no major changes between CV’s and the total charge enclosed by both the curves are probably similar to each other, illustrating the stable nature of electrode in the energy storage application.

material-sciences-engineering-curves-potential-cycles

Figure 4: CV curves for 1st and 1000th potential cycles.

Table 2 shows the percentage stability of supercapacitor for different electrolytes. It can be found that electrode can withstand about 1000 cycles without a significant decrease in the capacity, with various electrolytes, illustrating the stable nature in energy storage application. The specific capacitance values are decreased in small amount with the number of cycles due to the loss of active material [14]. Among the electrolytes KOH and KCL attained good cyclic stability of 88.90 and 90.01 respectively over 1000 cycles. It indicates that the material behave reversibly as an excellent capacitor material for large number of potential cycles.

Electrolytes Stability (%)
KOH 88.9
KCl 90.01
CH3CooNa 64.06
NH4Cl 60.24

Table 2: Percentage stability of with different electrolytes.

Electrochemical impedance analysis: Electrochemical Impedance Analysis was carried out to know the internal resistive parameters and capacitive behaviour of the supercapacitor at different operating open circuit potentials in KOH, KCl, CH3COONa and NH4Cl electrolytes each of 0.1 M concentration. Figure 5 shows the Nyquist plot of Z” vs. Z’ obtained by simulation using ZsimpWin software. The electrodes were excited with 5 mV AC signal and impedance was measured at open circuit potential in the frequency range from 1 Hz to 0.1 MHz [15].

material-sciences-engineering-nyquist-plots-electrolytes

Figure 5: Nyquist plots for various electrolytes.

The EIS figures show the small semicircle (first segment), Warburg diffusion line (second segment) and capacitive line (third segment). The beginning of the semicircle line (left-intercept of Z’’ at the Z’ axis) represents the resistance (Rs) of the electrolyte in contact with the current collector and electrode. The termination of the semicircle line (right-intercept of Z” at the Z’ axis) represents the internal resistance (Rp) of the electrode. The diameter of the semicircle (Rp- Rs) is equal to the ESR value. The second segment (straight line with a slope of approximately 45°) in the middle frequency region represents the combination of resistive and capacitive behaviours of the ions penetrating into the electrode pores. The length, slope and position of this segment appear to be different with each electrolyte. The third segment (straight lines sharply increasing at the low-frequency region) represents the dominance of capacitive behaviour from the formation of ionic and electronic charges of the electric double layer system at the micropore surfaces at this frequency, the ions can more easily diffuse into the micropores. The initiation point of this third segment line corresponds to the knee frequency (fk), and its corresponding resistance (Rk) is given by Z’k [16-20]. The values of fk and Rk are given in Table 3.

Electrolytes Rs (Ω) Rp (Ω) ESR (Ω) fk (Hz) Rk (Ω)
KOH 12 20 8 97 24.5
KCl 26.7 40.6 13.3 57.4 27.6
CH3COONa 143 160 17 31.6 174
NH4Cl 16.2 40 23.8 31.6 25.9

Table 3: Values of Rs, Rp, ESR, fk and Rk for different electrolytes.

The values of Rs, Rp, ESR, fk and Rk for all the electrolytes determined from the Figure 3 are listed in Table 3. The magnitude of the ESR value is found to be maximum for NH4Cl electrolyte. And minimum value of ESR is obtained for KOH electrolyte 8.0 Ω exhibiting highest specific capacitance.

Conclusion

Among the various aqueous electrolytes studied, KOH, KCl, CH3COONa and NH4Cl studied KOH revealed good electrochemical characteristics. For KOH electrolyte, the cell revealed specific capacitance of 675 Fgm-1. The specific capacitance values are decreased after 1000 cycles, but showed good reversible activity. For KCl electrolyte cyclic stability was 90.01% and for KOH it was 88.90. The magnitude of the ESR value is found to be minimal for KOH i.e, 8 Ω. From overall electrochemical analysis it was found that supercapacitor with 1% Mn doped cobalt oxide thin film electrode showed good electrochemical behaviour with KOH electrolyte.

References

Select your language of interest to view the total content in your interested language
Post your comment

Share This Article

Relevant Topics

Recommended Conferences

  • 10th International Conference on Emerging Materials and Nanotechnology
    July 27-29, 2017 Vancouver, Canada
  • 10th International Conference on Advanced Materials and Processing
    August 16-17 Edinburgh, Scotland
  • 3rd International Conference on Polymer Science and Engineering
    October 2-4, 2017 Chicago, USA
  • International Conference on Advanced Materials and Nanotechnology
    October 26-28, 2017 Osaka, Japan
  • 13th International Conference and Exhibition on Materials Science and Engineering
    November 13-15, 2017 Las Vegas, Nevada, USA
  • 14th International Conference on Functional Energy Materials
    December 06-07, 2017 Atlanta, USA

Article Usage

  • Total views: 111
  • [From(publication date):
    June-2017 - Jul 20, 2017]
  • Breakdown by view type
  • HTML page views : 88
  • PDF downloads :23
 
 

Post your comment

captcha   Reload  Can't read the image? click here to refresh

Peer Reviewed Journals
 
Make the best use of Scientific Research and information from our 700 + peer reviewed, Open Access Journals
International Conferences 2017-18
 
Meet Inspiring Speakers and Experts at our 3000+ Global Annual Meetings

Contact Us

Agri, Food, Aqua and Veterinary Science Journals

Dr. Krish

agrifoodaquavet@omicsonline.com

1-702-714-7001 Extn: 9040

Clinical and Biochemistry Journals

Datta A

clinical_biochem@omicsonline.com

1-702-714-7001Extn: 9037

Business & Management Journals

Ronald

business@omicsonline.com

1-702-714-7001Extn: 9042

Chemical Engineering and Chemistry Journals

Gabriel Shaw

chemicaleng_chemistry@omicsonline.com

1-702-714-7001 Extn: 9040

Earth & Environmental Sciences

Katie Wilson

environmentalsci@omicsonline.com

1-702-714-7001Extn: 9042

Engineering Journals

James Franklin

engineering@omicsonline.com

1-702-714-7001Extn: 9042

General Science and Health care Journals

Andrea Jason

generalsci_healthcare@omicsonline.com

1-702-714-7001Extn: 9043

Genetics and Molecular Biology Journals

Anna Melissa

genetics_molbio@omicsonline.com

1-702-714-7001 Extn: 9006

Immunology & Microbiology Journals

David Gorantl

immuno_microbio@omicsonline.com

1-702-714-7001Extn: 9014

Informatics Journals

Stephanie Skinner

omics@omicsonline.com

1-702-714-7001Extn: 9039

Material Sciences Journals

Rachle Green

materialsci@omicsonline.com

1-702-714-7001Extn: 9039

Mathematics and Physics Journals

Jim Willison

mathematics_physics@omicsonline.com

1-702-714-7001 Extn: 9042

Medical Journals

Nimmi Anna

medical@omicsonline.com

1-702-714-7001 Extn: 9038

Neuroscience & Psychology Journals

Nathan T

neuro_psychology@omicsonline.com

1-702-714-7001Extn: 9041

Pharmaceutical Sciences Journals

John Behannon

pharma@omicsonline.com

1-702-714-7001Extn: 9007

Social & Political Science Journals

Steve Harry

social_politicalsci@omicsonline.com

1-702-714-7001 Extn: 9042

 
© 2008-2017 OMICS International - Open Access Publisher. Best viewed in Mozilla Firefox | Google Chrome | Above IE 7.0 version